ABOSN PE outrigger pads crane mats plastic crane outrigger jack pad provide a super strong, rigid and easy to use foundation for a wide variety of outrigger enabled equipment. Constructed of engineered thermoplastic material, with a crush rating up to 750 psi and maximum allowable load ratings up to 300,000 lbs., ABOSN PE outrigger pads crane mats plastic crane outrigger jack pad deliver the strength, stiffness and reliability you can trust.
1. Different surface
A Smooth Surface B Circle in Middle C Rhombus pattern in surface D Anti-slip Surface
2. Handle
A : With nylon rope and rubber sleeve B : With hole holder on top C : With Steel Chain
3. Shape
A : Square shape B:Round shape
Applications
ABOSN PE outrigger pads crane mats plastic crane outrigger jack pad put under the support-leg Truck Crane, Crawler Crane, Rough Crane, Boom Pump, Concrete Pump, Fire Truck, Utility Truck, Tree Trimmer, Any type of Aerial Equipment and so on, for making the machine work safely.
--Highest abrasion resistance of any polymer, 6 times more abrasion resistant than steel
--Do not absorb moisture and will not swell up over time due to exposure outdoors.
--Good impact intensity,Do not lose their impact strength over time.
--Good breaking elongation,so they will bend but not break under extreme loads.
--Non-stick surface, easy to clean.
--Corrosion and chemical resistant.
--Noise- absorption, Vibration-absorption
--Super compression strength
--15 Percent the weight of steel pads and easier to handle
--Compressive loads up to one million pounds
--Up to 15,000 pounds per square foot
--Non-Conductive
--Non-Toxic and smell
Specification of UHMWPE plastic track lifts outrigger scaffolding support pads :
| No. | Dimension(mm) | Unit Weight | Load Capacity | No | Dimension (mm) | Unit Weight | Load Capacity |
| 1 | 300X300X30 | 2.7 | 5 | 14 | 500X500X60 | 15 | 30 |
| 2 | 400X400X30 | 4.8 | 10 | 15 | 600X600X60 | 21.60 | 40 |
| 3 | 300X300X40 | 3.6 | 8 | 16 | 800X800X60 | 38.40 | 50 |
| 4 | 400X400X40 | 6.4 | 15 | 17 | 1000X1000X60 | 60 | 80 |
| 5 | 400X400X40 | 10 | 18 | 18 | 1200X1200X60 | 84.60 | 100 |
| 6 | 600X600X40 | 14.4 | 30 | 19 | 600X600X80 | 28.8 | 65 |
| 7 | 1000X1000X40 | 40 | 40 | 20 | 800X800X80 | 51.20 | 80 |
| 8 | 400X400X50 | 8 | 18 | 21 | 1000X1000X80 | 80 | 120 |
| 9 | 500X500X50 | 12.5 | 20 | 22 | 1200X1200X80 | 115.20 | 150 |
| 10 | 600X600X50 | 18 | 35 | 23 | 2000X2000X80 | 320 | 170 |
| 11 | 800X800X50 | 32 | 40 | 24 | 1000X1000X100 | 100 | 120 |
| 12 | 1000X1000X50 | 50 | 55 | 25 | 1500X1500X100 | 225 | 150 |
| 13 | 1200X1200X50 | 72 | 60 | 26 | 2000X2000X100 | 400 | 180 |
Standard Size of UHMWPE Sheets( length width thickness):
UHMWPE Sheet 5000mm x 1300mm x 6~300mm
UHMWPE Sheet 3000mm x 1500mm x 6~300mm
UHMWPE Sheet 4700mm x 1200mm x 6~300mm
UHMWPE Sheet 4500mm x 2000mm x 6-400mm
UHMWPE Sheet 2000mm x 1000mm x 6-400mm
Application of UHMWPE / HDPE polyethylene plastic crane stabilizer boom wear pads .
Key properties of UHMWPE / HDPE polyethylene plastic crane stabilizer boom wear pads
ABOSN PE outrigger pads crane mats are available in three categories; Medium Duty (1.0″ thick), Heavy Duty (2.0″ thick) and Super Duty (3.0″ and 4.0″ thick) and are designed for equipment typically up to 100 tons in capacity.
As the thickness of a Xinxing PE outrigger pads crane mats increases it has a greater ability to distribute higher loads over the ground.
The size and thickness of the PE outrigger pads crane mats you need depends on your equipment type/specifications and the soil bearing capacity.
Techinal Data Sheet
| Property: | Test Method (Standard) | Ticona GUI4152 | Ticona GUI4150,4120 | Unit |
| Molecular weight | 3-5 million | 3-5 million | ||
| Density | ISO 1183-1:2012/DIN53479 | 0.92-0.98 | 0.93-0.98 | g/cm³ |
| Compression strength | ISO 604:2002 | ≥30 | ≥32 | Mpa |
| Tensile strength | ISO527-2:2012 | ≥20 | ≥22 | Mpa |
| Elongation at break | ISO527-2:2012 | ≥300 | ≥300 | % |
| Dynamic Friction coefficient | ASTM D 1894/GB10006-88 | ≤0.20 | ≤0.18 | |
| Dynamic Friction coefficient | ASTM D 1894/GB10006-88 | ≤0.20 | ≤0.18 | |
| Notched impact strength (Charpy) | ISO179-1:2010/GB/T 1043.1-2008 | ≥100 | ≥100 | kJ/m2 |
| Abrasion wear index | ES-X60210-2008 | ≤30 | ≤30 | mg |
| Vicat softing point | ISO306:2004 | ≥80 | ≥80 | °C |
| Hardness shore-D | ISO 868:2003 | 60-65 | 61-66 | D |